Transformation of Light Alkanes into High-Value Aromatics

This research work is focused on the transformation of light alkane (propane) into high-value aromatics using gallo-alumino-silicate catalysts. Two sets of gallo-alumino-silicates were synthesized for this study. In the first set, the ratio of Ga/(Al+Ga) was modified, while the Si/(Al+Ga) ratio was held constant. In the subsequent set, the Si/(Al+Ga) ratio was adjusted, while maintaining a consistent Ga/(Al+Ga) ratio. This approach aimed to directly assess the impact of each ratio on catalyst performance. The comprehensive characterization of all catalysts was conducted using various instrumental techniques, i.e., BET surface area, XRD, NH₃-TPD, ²⁷Al, ⁷¹Ga and ²⁹Si MAS NMR, and XPS. A gradual reduction in the percentage of crystallinity and rise in meso-surface area was noticed with a rise in Ga/(Al+Ga) ratio. The total acidity (NH₃-TPD) demonstrated a decline as the Si/(Al+Ga) ratio increased, attributed to an overall decline in Al³⁺ or Ga³⁺ species. The XPS intensity of the Ga 2p_3/2 peak rose in correlation with an elevated ratio of Ga/(Al+Ga), suggesting the formation of extra-framework Ga species. The propane conversion, aromatic yield, and aromatization/cracking ratio exhibited an increase with an increasing Ga/(Al+Ga) ratio, reaching an optimum value of 0.46 before declining. Conversely, an appreciable drop in the conversion of propane and yield of aromatics was detected with the rise in Si/(Al+Ga) ratio, attributing to the decline in acidity. The catalyst having a Ga/(Al+Ga) ration of 0.46 exhibited the highest propane conversion and aromatic yield of 83.0% and 55.0% respectively.