Properties of cement kiln dust concrete

This paper reports results of a study conducted to assess the properties of cement kiln dust (CKD) blended cement concretes. Cement concrete specimens were prepared with 0%, 5%, 10%, and 15% CKD, replacing ASTM C 150 Type I and Type V. The mechanical properties of CKD concrete specimens were evaluated by measuring compressive strength and drying shrinkage while the durability characteristics were assessed by evaluating chloride permeability and electrical resistivity. The compressive strength of concrete specimens decreased with the quantity of CKD. However, there was no significant difference in the compressive strength of 0 and 5% CKD cement concretes. A similar trend was noted in the drying shrinkage strain. The chloride permeability increased and the electrical resistivity decreased due to the incorporation of CKD. The performance of concrete with 5% CKD was almost similar to that of concrete without CKD. Therefore, it is suggested to limit the amount of CKD in concrete to 5% since the chloride permeability and electrical resistivity data indicated that the chances of reinforcement corrosion would increase with 10% and 15% CKD.