Physical properties of La³⁺ ion doped Ni[sbnd]Zn based spinel ferrite nanomaterials for technological applications

Spinel ferrite nanoparticles are extensively utilized in various everyday applications due to their exceptional capabilities. They are highly effective and efficient for various applications such as energy storage devices, microwave, electrode design, fuel cells, and recording media. Based on these applications, five samples of lanthanum doped nickel‑zinc spinel ferrite Ni_0.5Zn_0.5La_xFe_2-xO₄ nanoparticles were synthesized using the sol-gel auto-combustion technique. The lanthanum concentrations varied as x = 0.00, 0.05, 0.10, 0.15 and 0.20. X-ray diffraction (XRD) analysis revealed the formation of single phase cubic spinel structure of the prepared samples. The crystallite size was determined using the Scherrer formula and the values lies in the range of 9.22 to 20.09 nm. The chemical composition of the prepared samples was confirmed using Fourier transform infrared spectroscopy (FTIR) analysis. Transmission electron microscopy (TEM) confirmed the agglomeration and spherical shape morphology of the nanoparticles with an average particle size of 40 nm. Magnetic properties along with La³⁺ ion concentrations were investigated using the vibrating sample magnetometer (VSM). The dielectric properties of the prepared samples were carried out using impedance analyzer with an applied frequency ranging from 1 MHz to 3 GHz. Furthermore, the polarization mechanism in the applied frequency range was discussed with relaxation behavior at high frequency. The impact of La³⁺ concentrations on different parameters such as dielectric constant, impedance, electric modulus, tangent loss, and Ac conductivity were also investigated. The investigation of dielectric parameters. The relaxation mechanism at high frequency provided a significant impact of such type of materials to store energy due lake of hopping between the tetra and octahedral sites by addition of La³⁺ doping. The prepared samples exhibit excellent magnetic as well dielectric properties which makes suitable for microwave devices and soft magnetic applications.