Abstract
Platinum is diffused into the single-crystal superalloys CMSX-4 and CMSX-10 to integrate a surface protection layer consisting of a mixture of γ′- and γ-phases. It is shown that the Pt/CMSX-10 system is characterized by higher thermal stability and resistance to oxidation in comparison with the Pt/CMSX-4 system. Such difference is correlated with the initial microstructure and composition of the two systems and is reflected on their performance in thermal barrier coatings utilizing yttria-stabilized zirconia as top coating. Based upon cyclic oxidation tests, the Pt/CMSX-10 system is found to provide about threefold increase in useful life. However, both coatings are found to fail by spallation of the top coating due to decohesion of the thermally grown oxide developed by each system. It is concluded that the higher performance provided by the Pt/CMSX-10 stems from decelerated kinetics of interdiffusion and oxidation.
| Original language | English |
|---|---|
| Pages (from-to) | 4998-5008 |
| Number of pages | 11 |
| Journal | Journal of Materials Engineering and Performance |
| Volume | 28 |
| Issue number | 8 |
| DOIs | |
| State | Published - 15 Aug 2019 |
Bibliographical note
Publisher Copyright:© 2019, ASM International.
Keywords
- bond coatings
- electron microscopy
- microstructure
- oxidation
- superalloys
- thermal barrier coatings
ASJC Scopus subject areas
- General Materials Science
- Mechanics of Materials
- Mechanical Engineering