Effect of Graphite on the Mechanical and Petrophysical Properties of Class G Oil Well Cement

Casing cementing is one of the most crucial operations in the oil well drilling process since it determines the durability and stability of the well throughout its life. Different additives have been mixed into the oil well cement slurry to improve the properties of both the cement slurry and the solidified cement sheath. Graphite is a waste material with a huge potential to be utilized in cementing to improve the properties of the oil well cement and reduce the graphite waste content in the environment. This study intends to analyze the effect of graphite on alteration in properties of the cement compressive and tensile strength, Poisson’s ratio, Young’s modulus, porosity, and permeability for three days of curing. Based on the trend of the properties during the three days of curing, equations were established to describe the future change in cement properties with time. Two formulas of cement, the base (with no graphite) and graphite-based (with 0.2% by weight of cement graphite) were prepared in this study. The results showed that the graphite successfully increased the compressive strength, tensile strength, and Poisson’s ratio of the cement sheath, throughout the curing process. Young’s modulus was decreased after the incorporation of graphite which indicates an enhancement in cement resistance to shear forces. The porosity and permeability were also decreased indicating formation of a more densified cement sheath.