Dielectric study and ac conductivity of iron sodium silicate glasses

A series of glasses with formula (SiO₂)_0.7-x(Na ₂O)_0.3(Fe₂O₃)_x with (0.0 ≤ x ≤ 0.20) were prepared and studied by means of AC measurements in the frequency range 20 kHz to 13 MHz at room temperature. The study of frequency dependence of both dielectric constant ε' and dielectric loss ε" showed a decrease of both quantities with increasing frequency. The results have been explained on the basis of frequency assistance of electron hopping besides electron polarization. From the Cole-Cole diagram the values of the static dielectric constant ε_s, infinity dielectric constant ε_∞, macroscopic time constant τ, and molecular time constant τ_m are calculated for the studied amorphous samples. The frequency dependence of the ac conductivity obeys a power relation, that is σ_ac (ω) = Α ω^s. The obtained values of the constant s lie in the range of 0.7 ≤ s ≤ 1 in agreement with the theoretical value which confirms the simple quantum mechanical tunneling (QMT) model. The increase in ac conductivity with iron concentration is likely to arise due to structural changes occurring in the glass network. The structure of a glass with similar composition was published and showed clustering of Fe²⁺ and Fe³⁺ ions which favor electron hopping and provide pathways for charge transport.