Co on porous carbon network derived from ZIF-8 for oxygen reduction and evolution reaction in alkaline solution

Porous carbon wrapped on cobalt catalyst is one of the promising candidates to replace noble metal-based catalysts for ORR. Herein, a porous carbon network (PCN) was obtained by synthesis of zeolitic-imidazole frameworks (ZIF-8) followed by pyrolysis at 1050 ℃ under a nitrogenous atmosphere and the cobalt (Co) was deposited on PCN to obtain Co-PCN by sequential reduction method. The PCN showed a relatively high specific surface area of 806.43 m²/g and decreases to 329.4 m²/g with the introduction of Co contents in PCN. The Co-PCN reveals excellent performance having a current density of 350 mA cm⁻² for the ORR at 0.5 V after 20th cycles as a cathode material in rechargeable zinc-air batteries.